dc.description.abstractPenelitian ini menyintesis dan mencirikan membran polisulfon tersulfonasititanium dioksida (sPSf-TiO2). Sulfonasi dilakukan pada suhu 40 °C selama 60 menit menggunakan oleum sebagai agen sulfonasi dan TiO2 ditambahkan untuk meningkatkan kinerja membran. Derajat sulfonasi sebesar 47.5% dan morfologi membran menunjukkan bahwa tambahan TiO2 membuat membran lebih rapat dibandingkan tanpa tambahan TiO2. Membran yang dicirikan dengan spektrofotometer inframerah transformasi fourier menunjukkan puncak gugus sulfonat tertrisubtitusi 1,2,4- pada 1724 cm-1. Membran komposit diperoleh dengan menambahkan polisulfon tersulfonasi dengan TiO2 dengan ragam konsentrasi 3% dan 5%. Nilai konduktivitas dan beda potensial tertinggi dihasilkan pada membran sPSf-TiO2 5% dengan nilai berturut turut 1.07 × 10-3 S/cm dan 422 mV. Berdasarkan ciri tersebut, membran komposit sPSf-TiO2 dapat diaplikasikan untuk direct methanol fuel cell.en
dc.description.abstractThis experiment is to synthesize and to characterize sulfonated polysulfonetitanium dioxide composite membranes (sPSf-TiO2). The sulfonation was done in 40 °C for 60 minutes using oleum as the sulfonation agent and TiO2 was added to improve membrane performances. The degree of sulfonation through sulfonation process was 47.5% and the morphology of the membrane showed that the addition of TiO2 made the membrane denser than that without TiO2. The infared spectra showed there was 1,2,4- trisubstituted sulfonate group at 1724 cm-1. The composite membrane was produced by adding sulfonated polysulfone and TiO2 with concentration of 3% and 5%. The composite membrane sPSf-TiO2 5% gave the highest proton conductivity and voltage as of 1.07 × 10-3 S/cm and 422 mV, respectively. Based on the result, the composite membrane sPSf-TiO2 can be applied for direct methanol fuel cell system.en
dc.language.isoid
dc.publisherBogor Agricultural University (IPB)
dc.titleMembran komposit polisulfon tersulfonasi-titanium dioksida untuk aplikasi direct methanol fuel celen
dc.title.alternativeComposite of sulfonated polysulfone–titanium dioxide membrane for application on direct methanol fuel cellen
dc.typeUndergraduate Thesisen
dc.subject.keywordmembran kompositen
dc.subject.keywordpolisulfon tersulfonasien
dc.subject.keywordsel bahan bakaren
dc.subject.keywordtitanium dioksidaen