Sintesis dan Pencirian Natrium Titanat (Na2Ti2O4(OH)2) Berbahan Dasar Titanium Dioksida

Abstract

TiO2 can be utilized as basic material for synthesis of sodium titanate (Na2Ti2O4(OH)2). This research was purposed to synthesize and characterize sodium titanate from TiO2 rutile powder as a basic material. Sodium titanate was synthesized by hydrothermal process at temperature 130 °C by mixing TiO2 rutile powder with 5 M and 10 M NaOH solution, then each was calcinated at temperature 700 °C. The energy dispersive X-ray analysis showed that sodium titanate has been successfully synthesized. This result was also supported by functional group analysis with Fourier transform infrared (FTIR) spectrofotometer showing the existence of Ti-O-Na vibration band at 989.42 cm-1. The formation of sodium titanate was depend on the reaction condition such as temperature, reaction time, and NaOH concentration. Scanning electron microscope image indicated that sodium titanate synthesized at 130 °C in 20 hours reaction time with 10 M NaOH had crystal size of 99.37 nm.