| dc.description.abstract | Lignosulphonate, a modification product of lignin waste from pulp and paper industry can be used as water reducer in mortar mixture. This substance can influence the mechanical characteristic of mortar such as diameter of flow, flexural strength, compressive strength, and setting time of cement paste. Lignosulphonate shows it function as dispersant on cement hydration at 3 days that analyzed with x-ray difractometer. Research result show that flow of fresh mortar rise with increase concentration (from weight of cement) of synthetic sodium lignosulphonate (NaLS). It show that mortar homogenity also increasing. The result of flexural strength and compressive strength test use synthetic NaLS 0.1-0.3% from weight of cement show that addition synthetic NaLS 0.2% is the best result because it has the biggest of flexural strenght and compressive strength value. Initial setting time of cement paste increase, about 50% with addition of synthetic NaLS 0.2%. Whereas the final setting time decrease, about 8%. Cement hydration test show increase hydration product peak, Ca(OH)2 dan calcium silicate hydrate (C-S-H). | en |