Sintesis Zeoli! X dan Nanokomposit ZeolitJTi02dari Kaolin serta Aplikasinya pada Adsorpsi Fotodegradasi Biru Metilena
(2013)
Kaolin is rarely used as an adsorbent due to its low adsorption capacity. Therefore, kaolin was converted into zeolite and nanocomposite zeolitefri02. The products were then analyzed using x-ray diffraction and scanning ...
Sintesis Zeolit dan Nanokomposit Zeolit/TiO2 dari Abu Layang dan Waterglass serta Uji Adsorpsi dan Fotodegradasinya
(2013)
Coal fly ash contains 20.74% Si and 4.09% Al, rendering its possibility to be synthesized to zeolite. Zeolite was synthesized by smelting at 550 °C, and continued with hydrothermal method at 90 °C for 6 hours. The weighed ...
Sintesis Nanokomposit Kaolin/TiO2 Teremban Fe2O3 untuk Adsorpsi-Fotodegradasi Biru Metilena
(2013)
Kaolin is a type of clay mineral that has adsorption capacity. The experiment shows that the adsorption capacity of kaolin was 20.6 mg/g. This value is lower than zeolite adsorption capacity that in general has value above ...
Sintesis Zeolit P1 dan Nanokomposit Zeolit P1/TiO2 dari Abu Terbang Batu Bara dan Sekam Padi serta Uji Kemampuan Adsorpsi dan Fotodegradasinya
(2013)
Abu terbang merupakan limbah dari pembangkit listrik tenaga uap (PLTU) batu bara yang memiliki kandungan silika dan alumina yang cukup tinggi. Sekam merupakan limbah dari penggilingan padi yang mengandung kandungan silika ...
Nanokomposit kaolin-TiO2 dengan dopan urea untuk adsorpsi dan fotodegradasi zat warna biru metilena
(2013)
Methylene blue is one type of dyes found as pollutant in Indonesia water system. Kaolin-TiO2 nanocomposite was synthesized and used to overcome this problem by utilizing its adsorption-photodegradation mechanism. Kaolin-TiO2 ...
Adsorpsi–fotodegradasi Biru Metilena oleh Nanokomposit Kaolin/TiO2 yang Diemban dengan ZnO
(2013)
Synthetic dye waste such as methylene blue pollutes aquatic evironment. Kaolin/TiO2 nanocomposite was made for adsorption–photodegradation process under UV light. The nanocomposite was prepared by paste and ball milling ...