dc.description.abstract | Jerami padi hanya dianggap sebagai limbah pertanian yang dimanfaatkan
untuk bahan pakan ternak. Akantetapi dalam abu jerami padi terdapat kandungan
silika yang cukup tinggi, sehingga jerami padi sangat potensial menjadi bahan baku
pembuatan nanosilika. Salah satu metode yang digunakan untuk mendapatkan
nanosilika adalah metode hidrotermal. Tujuan penelitian ini adalah mensintesis
nanosilika dari jerami padi dengan mengetahui pengaruh suhu dalam proses
hidrotermal terhadap karakteristik nanosilika. Variasi suhu proses hidrotermal yang
digunakan yaitu 150 °C, 200 °C, dan 250 °C dengan waktu proses selama 4 jam.
Ketiga sampel yang berada pada fase amorf, dengan memiliki derajat kristalinitas
berturut-turut adalah 27,42%, 19,32%, dan 20,42%. Ukuran partikel sampel yang
disintesis dengan variasi suhu 150 °C, 200 °C, dan 250 °C masing-masing memiliki
rata-rata sebesar 785,59 nm, 11,50 nm, dan 695,39 nm. Sampel yang disintesis
dengan suhu 250 °C memiliki distribusi ukuran yang lebih seragam dibandingkan
dengan sampel yang disintesis suhu 150 °C dan 200 °C. Karakteristik sifat listrik
pada ketiga sampel yaitu material semikonduktor pada frekuensi rendah, frekuensi
sedang, dan frekuensi tinggi. | id |
dc.description.abstract | Rice straw are considered as an agricultural waste used for fodder.But, in the ashes of rice straw lies a considerable concentration of silica, so rice straw is potential as a raw material for making nanosilica. One method for obtain nanosilica is hydrothermal method. The purpose of this study was to synthesize nanosilica of rice straw by knowing how the temperature in the hydrothermal process affects the characteristics of the nanosilica. The variation of the temperature of the hydrothermal process used 150 °C, 200 °C, and 250 °C with the processing time for 4 hour. All three samples are on the amorphous phase that were had a crystallinity of 27,42%, 19,32%, and 20,42%. samples. The particle size of each samples has an average size 785,59 nm, 11,50 nm, and 695,39 nm. The particle size of sample synthesized at 250 °C was more uniform than sample synthesized at 150 °C and 200 °C. The characteristics of the electrical properties are likely to semiconductor materials at low frequency, moderate frequency, and high frequency. Keywords: Amorf, electrinical properties, hidrotermal, rice straw, size of nanosilica. | id |
dc.language.iso | id | id |
dc.publisher | IPB University | id |
dc.title | Sintesis Nanosilika dari Jerami Padi (Oriza sativa L.) dengan Variasi Suhu Proses Hidrotermal | id |
dc.title.alternative | Synthesis of Nanosilica from Rice Straw (Oriza sativa L.) with Variance of Temperature of Hydrothermal | id |
dc.type | Undergraduate Thesis | id |
dc.subject.keyword | Amorf | id |
dc.subject.keyword | electrinical properties | id |
dc.subject.keyword | hidrotermal | id |
dc.subject.keyword | rice straw | id |
dc.subject.keyword | size of nanosilica | id |