      Effect of Interlayer Caution Valence on Formation and Chemical Characteristics of Aluminumhydroxy-Vermuculite

      Thumbnail
      View/Open
      e-Journal (369.4Kb)
      Date
      2005
      Author
      Iskandar
      Metadata
      Show full item record
      Abstract
      Aluminumhydroxy-smectite (AHS), known also as pillared clay, has some specific c...haracteristics such as: wide specific surface area, high basal spacing, and stable at significant high temperature. The AHS was produced from smectite and polymer aluminum-hydroxy. In industrial sector, this product can be used as cracking-catalyst, absorber, and molecular sieve up to 500°C. Similar product can be constructed from vermiculite, and the aluminumhydroxy-vermiculite (AHV) is predicted have a better thermal stability than AHS due to higher charge density of vermiculite that adsorb more aluminumhydroxy than that of smectite. Related to the above background the objectives of the research were to study the effects of cation valence in the interlayer space of vermiculite using Li and Ml ions in the formation process and the chemical characteristics of AHV. Liand Mg-vermiculites with different particle sizes are reacted with polymer aluminum-hydroxy' at 100°C temperature. Solution of 2% Locron was used as source of aluminum-hydroxy. The products were characterized chemically and mineralogica/~v. The chemical characteristic includes total chemical analysis, whereas the mineralogical characteristic comprises basal spacing identification that was measured with X-ray diffractometer (XRD). The results indicated that the AHV producedfrom Li-vermiculite showed peaks of 1.86 nm and 1.41-1.45 nm with increasing intensity of the 1.86 nm peaks as the particle size was finer. The AHV produced from Mg-vermiculite showed only peak of 1.45 nm, whereas the 1.84 nm peak can on~v be identified as a shoulder. The AHV with peak of 1.86 nm (AHV-I.86) can keep its basal spacing to 1.68 nm after 3 hours heating at temperature of 700°C, whereas the AHV-I.45 nm shrinkages to 1.10/0.98 nm at the same treatments. Chemical analysis showed that the inter/oyer space of the AHV-I.86 consists more aluminum-hydroxy than that of the AHV-I.45. Ratio o(OH/AI o(the interlayer aluminum-hydroxy in the AHV-1.86 was 2.57, whereas that of the AHV-I.45 was 2.40.
      URI
      http://repository.ipb.ac.id/handle/123456789/43737
      Collections
      • Jurnal Ilmu Tanah & Lingkungan [54]

      Copyright © 2020 Library of IPB University
      All rights reserved
      Contact Us | Send Feedback
      Indonesia DSpace Group 
      IPB University Scientific Repository
      UIN Syarif Hidayatullah Institutional Repository
      Universitas Jember Digital Repository
        

       

      Browse

      All of IPB RepositoryCollectionsBy Issue DateAuthorsTitlesSubjectsThis CollectionBy Issue DateAuthorsTitlesSubjects

      My Account

      Login

      Application

      google store

      Copyright © 2020 Library of IPB University
      All rights reserved
      Contact Us | Send Feedback
      Indonesia DSpace Group 
      IPB University Scientific Repository
      UIN Syarif Hidayatullah Institutional Repository
      Universitas Jember Digital Repository