| dc.contributor.advisor | Charlena | |
| dc.contributor.advisor | Suparto, Irma Herawati | |
| dc.contributor.author | Hastiwi, Shalma Pulung | |
| dc.date.accessioned | 2021-08-29T06:39:10Z | |
| dc.date.available | 2021-08-29T06:39:10Z | |
| dc.date.issued | 2021 | |
| dc.identifier.uri | http://repository.ipb.ac.id/handle/123456789/108908 | |
| dc.description.abstract | Kerusakan tulang yang meningkat membutuhkan sintesis biomaterial sebagai bahan implan. Penelitian ini dilakukan untuk meninjau berbagai referensi mengenai penyalutan komposit HAp-kitosan-logam oksida pada paduan logam. Metode yang baik dan banyak dipilih dalam sintesis HAp-kitosan-logam oksida yakni dengan menggunakan metode presipitasi, ex-situ dan metode elektroforesis deposisi (EPD) sebagai metode penyalutannya. Paduan logam yang tersalut komposit HApkitosan-logam oksida memiliki potensi dalam menghasilkan implan yang mampu menghambat bakteri dan ketahanan korosi secara baik. Komposit HAp-ZnOkitosan memiliki zona hambat paling baik terhadap bakteri E. coli yakni sebesar 8 mm. Zona hambat juga dipengaruhi oleh konsentrasi logam oksida yang ditambahkan. Paduan logam yang telah tersalut komposit menunjukkan ketahanan korosi lebih baik dibandingkan sebelum penyalutan. Logam CoCrMo yang tersalut komposit HAp-kitosan memiliki ketahanan korosi paling baik dibandingkan logam Stainless Steel dan Ti6Al4V dengan nilai laju korosi sebesar 0,0035 mpy. | id |
| dc.description.abstract | Increased bone destruction requires the synthesis of biomaterials as implant materials. This research was conducted to review various references regarding the coating of HAp-metal oxide-chitosan composites on metal alloys. A good and widely chosen method in the synthesis of HAp-chitosan-metal oxide is by using precipitation, ex-situ and deposition electrophoresis (EPD) methods as coating methods. The metal alloy coated with the HAp-chitosan-metal oxide composite has the potential to produce implants that can inhibit bacteria and have good corrosion resistance. The HAp-ZnO-chitosan composite had the best inhibition zone against E. coli bacteria, which was 8 mm. The zone of inhibition also affects the concentration of added metal oxides. The composite coated alloy showed better corrosion resistance than before coating. CoCrMo metal coated with HAp-chitosan composite has the best corrosion resistance compared to Stainless Steel and Ti6Al4V with a corrosion rate of 0,0035 mpy. | id |
| dc.language.iso | id | id |
| dc.publisher | IPB University | id |
| dc.title | Kajian Komposit Hidroksiapatit-Kitosan dengan Berbagai Logam Oksida yang Disalutkan pada Paduan Logam Sebagai Material Implan | id |
| dc.title.alternative | Study of Hydroxyapatite-Chitosan Composites with Various Metal Oxides Coated on Metal Alloys as Implant Materials | id |
| dc.type | Undergraduate Thesis | id |
| dc.subject.keyword | alloy | id |
| dc.subject.keyword | antibacterial | id |
| dc.subject.keyword | anticorrosion | id |
| dc.subject.keyword | hydroxyapatite-chitosan | id |
| dc.subject.keyword | metal oxide | id |